Silicon carbide foam ceramic filters can effectively stabilize the metal pouring process and suppress turbulence in molten metal. As the metal flows through their unique three-dimensional mesh channels, intense turbulence is efficiently converted into laminar flow. This laminar filling pattern significantly enhances the metal's ability to fill complex mold cavities, not only reducing erosion and scouring on mold walls and sand cores but also minimizing secondary oxidation and slag inclusion caused by turbulence, thereby significantly lowering casting defects and scrap rates.
0536-6427866
Shandong Yongchuang Material Technology Co., Ltd
产品特点
适用于铸铁、有色金属等生产领域，可使用温度高达1540℃。
具有良好的耐金属溶液冲刷性能。
高效过滤较小的非金属杂质，改善铸件表面和内在质量。
质量稳定，孔隙率高，过滤效果好。
性能指标
| 常温耐压强度≥（Mpa） | 体积密度（g/cm³） | 空隙率 % | 使用温度≤（℃） | 适应范围 |
|---|---|---|---|---|
| 1.2 | 0.36-0.45 | ≥ 80 | 1480 | 球铁、灰铁件 |
| 1.5 | 0.40-0.50 | ≥ 80 | 1500 | 较大球铁件 |
| 1.2 | 0.36-0.45 | ≥ 80 | 1450 | 有色合金、灰铁件 |
| 1.2 | 0.31-0.39 | ≥ 80 | 1480 | 高通过率 |
| 1.5 | 0.42-0.50 | ≥ 80 | 1500 | 大型球铁、碳钢件 |
常用尺寸
| 方型（mm） | 30×50×22 | 40×40×22 | 50×50×22 | 75×50×22 | 100×50×22 |
|---|---|---|---|---|---|
| 75×75×22 | 100×75×22 | 100×100×22 | 150×100×22 | 150×150×40 | |
| 300×150×40 | 125×125×30 | 120×120×25 | 80×80×22 | 90×90×22 | |
| 圆形（mm） | 40×15 | 50×22 | 60×22 | 70×22 | 80×22 |
| 90×22 | 100×22 | 125×25 | 150×30 | 200×40 |
尺寸选择
◎直径/边长40-70mm，厚度15-22mm
◎直径/边长75-100mm，厚度22-25mm
◎直径/边长125-150mm，厚度25-30mm
◎直径/边长175-225mm，厚度30-35mm
◎直径/边长250-300mm，厚度35-40mm
过滤能力
过滤量与铸件类型、放置位置、浇筑温度、压头大小等因素有关，具体使用方案与我司联系。
| 碳钢及低合金钢 | 1.0~2.7KG/cm² | 不锈钢 | 1.0~4.0KG/cm² |
孔径选择
中大铸钢件选择10~15ppi，要求较高的小件可以根据需求选择更小孔径过滤器。